Output from Program DRAGON-WWW

Generation of hkl and 2q

Silicon Standard

Cell parameters

a (Å) b (Å) c (Å) a (°) b (°) g (°) V (Å³)
5.43100 5.43100 5.43100 90.000 90.000 90.000 160.2

Wavelength = 1.54056 Å 2q Maximum = 130.000° Zero Error = 0.000° Minimum d-spacing = 0.84991 Å

Space group is Fd-3m Lattice = F 1^st symbol = d 2^nd symbol = -3 3^rd symbol = m Crystal class is m -3 m

Reflection conditions are hkl: k + l = 2n hkl: h + l = 2n hk0: h + k = 4n h0l: h + l = 4n

Number of generated reflections is 13 Number output to browser is 13

h k l J d (Å) 2q (°) h k l J d (Å) 2q (°) h k l J d (Å) 2q (°)

1 1 1 8 3.1356 28.441 3 3 1 24 1.2460 76.373 5 3 1 48 0.9180 114.086

2 2 0 12 1.9201 47.301 4 2 2 24 1.1086 88.026 4 4 2 24 0.9052 116.637

3 1 1 24 1.6375 56.120 5 1 1 24 1.0452 94.948 6 2 0 24 0.8587 127.536

2 2 2 8 1.5678 58.854 3 3 3 8 1.0452 94.948

4 0 0 6 1.3578 69.127 4 4 0 12 0.9601 106.703

Back (or use back button on browser to keep contents of form intact)

Author(s): Jeremy Karl Cockcroft

a (Å)	b (Å)	c (Å)	a (°)	b (°)	g (°)	V (Å³)
5.43100	5.43100	5.43100	90.000	90.000	90.000	160.2

h	k	l	J	d (Å)	2q (°)	h	k	l	J	d (Å)	2q (°)	h	k	l	J	d (Å)	2q (°)
1	1	1	8	3.1356	28.441	3	3	1	24	1.2460	76.373	5	3	1	48	0.9180	114.086
2	2	0	12	1.9201	47.301	4	2	2	24	1.1086	88.026	4	4	2	24	0.9052	116.637
3	1	1	24	1.6375	56.120	5	1	1	24	1.0452	94.948	6	2	0	24	0.8587	127.536
2	2	2	8	1.5678	58.854	3	3	3	8	1.0452	94.948
4	0	0	6	1.3578	69.127	4	4	0	12	0.9601	106.703